베마이트를 이용한 UF 세라믹 분리막의 제조

초록

A single layer ultrafiltration(UF) ceramic membrane was prepared using boehmite sol. Boehmite was synthesized using a typical sol-gel process with optimization of the viscosity, pH, molar ratio of aluminum isopropoxide(AIP) and HNO3. Boehmite sol was coated on a microfiltration(MF) support using the dip-coating method. MF support was dipped into the boehmite sol with a withdrawal speed of 5 mm/s and was maintained for 10 s in the boehmite sol, resulting in a uniform UF membrane layer of 10 μm thickness. The porosity of the obtained membrane was measured and found to be 41.2%; the pore size was found to range from 80~100 nm, corresponding to the pore size of the UF membrane. The flux of the obtained membrane was initially 540 L/m2 h and approximately 85% of the initial flux was recovered using a periodic back-flushing process.