화학적 방법에 의한 나노 시멘트 개발에 관한 기초 연구

초록

Advanced industries-IT, BT, NT and ET are rapidly developing in 21 century. And the cement industry is becoming the principal factor in air pollution because of the creation of CO2 during manufacturing. Also, the cement industry will be faced with a crisis due to the exhaustion of natural resources. In this study, nano cement by Bottom-up method of a chemical synthesis was developed. The generation of CO2 during the plasticization process of cement manufacturing was avoided. The purpose was to produce building materials that have both high strength and durability as the high value-added growth engine industry of the 21 century. The nano cement was developed using hydrothermal synthesis. This is a method of mixing after ripening, by manufacturing the high density gel and low gel, which does not require special test equipment or pressure conditions to produce. Particle size, SEM, EDX, and porosity tests were conducted. This study investigated the compressive strength of concrete with various compositions. Specimens were tested for compressive strength at 3, 7, 14 and 28days. The medium-sized (50% by weight) cement particles created by chemical synthesis were less than 168 nm. The compressive strength of the mortar prepared using this cement was 53.9 MPa. But it was judged that succeeding study will be necessary for development of nano building materials with high ability and economical analysis.

키워드