초음파의 비선형 특성을 이용한 SUS316L 재료의 피로 열화 평가에 관한 연구

초록

This study evaluated the fatigue degradation in a SUS316L specimen using the nonlinear ultrasonic method. The nonlinearity of the ultrasonic wave was estimated by a relative nonlinear parameter defined as the ratio of the amplitudes for the fundamental wave to the second harmonic wave. In the experiment, a measurement system with contact transducers was constructed; reliable measurements were assured by keeping measurement conditions consistent and reducing extra harmonics generated in the measurement system. Two types of SUS316L specimen were used in experiments; a rotating bar fatigue specimen and a tensile fatigue specimen. The fatigue condition used was high cycle fatigue. The former specimen had a cylindrical shape and was used to observe the change in the nonlinear parameter after fatigue accumulation in a specimen. The latter was a plate-shaped specimen and was used to confirm the change in the nonlinear parameter at the position where the fatigue stress was concentrated. The measured nonlinear parameter showed a strong correlation to the damage level in both fatigue tests.

키워드