Ultrathin Co-O oxide layer-driven perpendicular magnetic anisotropy in a CoO/[Co/Pd](m) multilayer matrix upon annealing

초록

Ferromagnetic/noble metal multilayer (ML) frames are expected to serve as reliable building blocks in a variety of perpendicular magnetic anisotropy (PMA) based spintronic devices. However, ultrathin ML matrices are highly susceptible to unintended reduction of electron spin polarization in the as-grown or annealed states and often require a large repeat number. Here, we introduce a simple approach to achieve thermally stable PMA in ultrathin [Co/Pd](3) MLs involving the incorporation of an ultrathin CoO capping layer. The thickness and oxygen content of the CoO layer are critical parameters to achieve enhanced PMA in ultrathin [Co/Pd](3)/CoO MLs post-annealed up to 400 degrees C. An extensive analysis of structural features identified that robust PMA characteristics in [Co/Pd](3)/CoO MLs are linked with thermally activated oxygen atom diffusion leading to structural reconfiguration upon annealing. The possible origin of the enhanced PMA in our [Co/Pd](3)/CoO ML samples after high-temperature annealing is discussed, thereby enabling their use in future spintronic-related devices.

키워드