Isothermal calorimetry investigation of Li1+xMn2-yAlzO4 spinel

초록

The heat generation of LiMn2O4, Lil(1.56)Mn(1.844)O(4), and Li1.06Mn1.89Al0.05O4 spinel cathode materials in a half-cell system was investigated by isothermal micro-calorimetry (IMC). The heat variations of the Li/LiMn2O4 cell during charging were attributed to the LiMn2O4 phase transition and order/disorder changes. This heat variation was largely suppressed when the stoichiometric spinel was doped with excess lithium or lithium and aluminum. The calculated entropy change (dE/dT) from the IMC confirmed that the order/disorder change of LiMn2O4, which occurs in the middle of the charge, was largely suppressed with lithium or lithium and aluminum doping. The dE/dT values obtained did not agree between the charge and the discharge at room temperature (25 degrees C), which was attributed to cell self-discharge. This discrepancy was not observed at low temperature (10 degrees C). Differential scanning calorimeter (DSC) results showed that the fully charged spinel with lithium doping has better thermal stability.

키워드