Capacity Degradation Mechanism and Cycling Stability Enhancement of AIF(3)-Coated Nanorod Gradient Na[Ni0.65Co0.08Mn0.27]O-2 Cathode for Sodium-Ion Batteries

초록

O3-type Na[NixCoyMnz]O-2 materials are attractive cathodes for sodium-ion batteries because of their full cell fabrication practicality, high energy density, and relatively easy technology transfer arising from their similarity to Li[NixCoyMnz]O-2 materials, yet their performance viability with Ni-rich composition (x >= 0.6) is still doubtful. More importantly, their capacity degradation mechanism remains to be established. In this paper, we introduce an O3-type Ni-rich AIF(3)-coated nanorod gradient Na[Ni0.65Co0.08Mn0.27]O-2 cathode with enhanced electro-chemical performance in both half-cells and full cells. AIF(3)-coated nanorod gradient Na[Ni0.65Co0.08Mn0.27]O-2 particles were synthesized through a combination of dry ball-mill coating and columnar composition gradient design and deliver a discharge capacity of 168 mAh g(-1) with 90% capacity retention in half cells (50 cycles) and 132 mAh g(-1) with 90% capacity retention in full cells (200 cycles) at 75 mA g(-1) (0.5C, 1.5-4.1 V). Through analysis of the cycled electrodes, the capacity-degradation mechanism was unraveled in O3-type Ni-rich Na[NixCoyMnz]O-2 from a structural perspective with emphasis on high-resolution transmission electron microscopy, providing valuable information on improving O3-type Na[NixCoyMnz]O-2 cathode performance.

키워드